Surface relief formation in Ge5As37S58–Se nanomultilayers

Achimova, E. та Stronski, A.V. та Paiuk, A. та Abaskin, V. та Meshalkin, A. та Prisacar, A. та Triduh, G. та Литвин, Оксана Степанівна (2015) Surface relief formation in Ge5As37S58–Se nanomultilayers Journal of Non-Crystalline Solids, 409. с. 43-48. ISSN 0022-3093

Повний текст недоступний з цього архіву. (Запит копії)
Офіційне посилання: http://www.journals.elsevier.com/journal-of-non-cr...

Анотація

For the first time direct one-step relief formation of holographic grating with the use of amorphous chalcogenide nanomultilayers of new composition based on Ge5As37S58–Se was studied. Amorphous Ge5As37S58–Se nanomultilayers were prepared by cyclic thermal vacuum deposition. Optical constants of Ge5As37S58–Se nanomultilayers, Ge5As37S58 and α-Se films were obtained from transmission spectra. AFM and Raman investigations were performed for morphology and structural characterization on pointed films. Holographic diffraction gratings with diffraction efficiency of 18% in transmission measured at wavelength λ = 650 nm were directly recorded in one step without etching. High quality of grating sinusoidal relief up to ~ 100 nm groove depth was studied by AFM.

Тип елементу : Стаття
Додаткова інформація: 10.1016/j.jnoncrysol.2014.11.010
Ключові слова: Surface relief; Amorphous chalcogenide; Nanomultilayers; Holographic grating
Типологія:
Підрозділи: Це архівні підрозділи Київського університету імені Бориса Грінченка > Кафедра інформатики
Користувач, що депонує: Оксана Степанівна Литвин
Дата внесення: 02 Бер 2015 14:00
Останні зміни: 11 Квіт 2018 07:16
URI: https://elibrary.kubg.edu.ua/id/eprint/6879

Actions (login required)

Перегляд елементу Перегляд елементу